Morphology and growth of carbon nanotubes catalytically synthesised by premixed hydrocarbon-rich flames

Chong, Cheng Tung, Tan, Win Hon, Lee, Siew Ling, Chong, William Woei Fong, Lam, Su Shiung and Valera Medina, Agustin ORCID: https://orcid.org/0000-0003-1580-7133 2017. Morphology and growth of carbon nanotubes catalytically synthesised by premixed hydrocarbon-rich flames. Materials Chemistry and Physics 197 , pp. 246-255. 10.1016/j.matchemphys.2017.05.036

[thumbnail of 170809 CNTs.pdf]
Preview
PDF - Accepted Post-Print Version
Download (1MB) | Preview

Abstract

Synthesis of carbon nanotubes (CNTs) was performed by using a laminar premixed flame burner at open atmospheric condition. The growth of CNTs on the substrate was supported catalytically by a transition metal under high temperature, hydrocarbon-rich environment. Analysis of the CNTs using high resolution electron microscope reveals the structure of synthesised nano-materials in disarray, clustered and tubular form. The graphitic structure of the CNTs are rather similar for all fuel-rich equivalence ratios tested, with an average diameter of ∼11–13 nm. Removal of the amorphous carbon and catalyst in the CNTs was performed via purification treatment using H2O2 and HCl solutions. Detail characterisation indicates the oxidation temperature of purified CNTs ranges between 497 and 529 °C. Deconvolution of the Raman spectra in the range of 900–1800 cm−1 shows the distinct characteristic bands of CNTs with IG/ID ratio of 0.66–0.72 for all the samples tested. In addition, the high level carbon concentration and sp2 Csingle bondC bond in the CNTs is shown by X-ray photoelectron spectroscopy analysis. The present study demonstrates that CNTs can be effectively synthesised from fuel-rich hydrocarbon flames at ϕ = 1.8–2.0 supported by nickel-based substrate.

Item Type: Article
Date Type: Publication
Status: Published
Schools: Engineering
Subjects: T Technology > TD Environmental technology. Sanitary engineering
Uncontrolled Keywords: Carbon nanotubes; Flame synthesis; Raman spectroscopy; TEM; CNT morphology; XPS
Publisher: Elsevier
ISSN: 0254-0584
Date of First Compliant Deposit: 30 May 2017
Date of Acceptance: 20 May 2017
Last Modified: 06 Nov 2023 21:31
URI: https://orca.cardiff.ac.uk/id/eprint/100944

Citation Data

Cited 26 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item

Downloads

Downloads per month over past year

View more statistics