Anchoring highly dispersed metal nanoparticles by strong electrostatic adsorption (SEA) on a dealuminated beta zeolite for catalysis

Zou, Run, Bramley, Gabriel A., Xu, Shanshan, Chansai, Sarayute, Panchal, Monik, Chen, Huanhao, Zhou, Yangtao, Gao, Pan, Hou, Guangjin, Holmes, Stuart M., Hardacre, Christopher, Jiao, Yilai, Logsdail, Andrew J. ORCID: https://orcid.org/0000-0002-2277-415X and Fan, Xiaolei 2024. Anchoring highly dispersed metal nanoparticles by strong electrostatic adsorption (SEA) on a dealuminated beta zeolite for catalysis. Catalysis Science & Technology 14 , pp. 164-173. 10.1039/d3cy01334k

PDF - Published Version Available under License Creative Commons Attribution. Download (2MB)

Abstract

Zeolites with defects can be combined with appropriate synthetic protocols to beneficially stabilise metallic clusters and nanoparticles (NPs). In this work, highly dispersed Ni NPs were prepared on a defect-rich dealuminated beta (deAl-beta) zeolite through strong electrostatic adsorption (SEA) synthesis, which enabled strong interactions between the electronegative deAl-beta and cationic metal ammine complexes (e.g., Ni(NH3)62+) via the framework silanol nests. Ni NPs with diameters of 1.9 ± 0.2 nm were formed after SEA and reduction in H2 at 500 °C and showed good activity in CO2 methanation (i.e., specific reaction rate of 3.92 × 10−4 mol s−1 gNi−1 and methane selectivity of 99.8% at 400 °C under GHSV of 30 000 mL g−1 h−1). The mechanism of the SEA synthetic process was elucidated by ex situ XAFS, in situ DRIFTS, and DFT. XAFS of the as-prepared Ni catalysts (i.e., unreduced) indicates that SEA leads to the exchange of anions in Ni precursors (e.g., Cl− and NO3−) to form Ni(OH)2, while in situ DRIFTS of catalyst reduction shows a significant decrease in the signal of IR bands assigned to the silanol nests (at ∼960 cm−1), which could be ascribed to the strong interaction between Ni(OH)2 and silanol nests via SEA. DFT calculations show that metallic complexes bind more strongly to charged defect sites compared to neutral silanol nest defects (up to 150 kJ mol−1), confirming the enhanced interaction between metallic complexes and zeolitic supports under SEA synthesis conditions. The results provide new opportunities for preparing highly dispersed metal catalysts using defect-rich zeolitic carriers for catalysis.

Item Type:	Article
Date Type:	Publication
Status:	Published
Schools:	Chemistry Cardiff Catalysis Institute (CCI)
Additional Information:	License information from Publisher: LICENSE 1: URL: http://creativecommons.org/licenses/by/3.0/, Start Date: 2023-11-27
Publisher:	Royal Society of Chemistry
ISSN:	2044-4753
Date of First Compliant Deposit:	5 December 2023
Date of Acceptance:	27 November 2023
Last Modified:	13 Feb 2024 14:42
URI:	https://orca.cardiff.ac.uk/id/eprint/164532

Actions (repository staff only)

Edit Item