Borrell, Amparo, Salvador, María Dolores, Garcia Rocha, Victoria ORCID: https://orcid.org/0000-0001-6125-8556, Fernández, Adolfo, Molina, Tamara and Moreno, Rodrigo 2013. Enhanced properties of alumina-aluminium titanate composites obtained by spark plasma reaction-sintering of slip cast green bodies. Composites: Part B Engineering 47 , pp. 255-259. 10.1016/j.compositesb.2012.11.010 |
Abstract
Full dense alumina + 40 vol.% aluminium titanate composites were obtained by colloidal filtration and fast reaction-sintering of alumina/titania green bodies by spark plasma sintering at low temperatures (1250–1400 °C). The composites obtained had near-to-theoretical density (>99%) with a bimodal grain size distribution. Phase development analysis demonstrated that aluminium titanate has already formed at 1300 °C. The mechanical properties such as Vickers hardness, flexural strength and fracture toughness of bulk composites are significantly higher than those reported elsewhere, e.g. the composite sintered at 1350 °C show values of about 24 GPa, 424 MPa and 5.4 MPa m1/2, respectively. The improved mechanical properties of these composites are attributed to the enhanced densification and the finer and more uniform nanostructure achieved by non-conventional fast sintering of slip-cast dense green compacts.
Item Type: | Article |
---|---|
Date Type: | Publication |
Status: | Published |
Schools: | Engineering |
Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
Publisher: | Elsevier |
ISSN: | 1359-8368 |
Date of Acceptance: | 13 November 2012 |
Last Modified: | 01 Nov 2022 10:57 |
URI: | https://orca.cardiff.ac.uk/id/eprint/93343 |
Citation Data
Cited 23 times in Scopus. View in Scopus. Powered By Scopus® Data
Actions (repository staff only)
Edit Item |