Microstructural control of ultrafine and nanocrystalline WC?12Co?VC/Cr3C2 mixture by spark plasma sintering

Bonache, V., Salvador, M.D., Garcia Rocha, Victoria ORCID: https://orcid.org/0000-0001-6125-8556 and Borrell, A. 2011. Microstructural control of ultrafine and nanocrystalline WC?12Co?VC/Cr3C2 mixture by spark plasma sintering. Ceramics International 37 (3) , pp. 1139-1142. 10.1016/j.ceramint.2010.11.026

Full text not available from this repository.

Abstract

The aim of this present work is to study the effect of VC and/or Cr3C2 in densification, microstructural control and mechanical behaviour of WC–12Co ultrafine and nanocrystalline mixtures, consolidated by spark plasma sintering at 1100 °C, applying a pressure of 80 MPa in combination with a heating rate of 100 °C min−1. Nanocrystalline and ultrafine mixtures with an average size of 30 nm and 100–250 nm, respectively, with the addition of 1 and 0.5 wt.% of VC/Cr3C2 grain growth inhibitors, respectively, were investigated. The density, microstructure, hardness and fracture toughness of the consolidated samples were measured and observed. The addition of VC inhibitor allows an excellent grain growth control keeping microstructures with an average grain size of 154 nm. The hardness values and fracture toughness obtained were about 2000 HV30 and above 10 MPa m1/2, respectively.

Item Type: Article
Date Type: Publication
Status: Published
Schools: Engineering
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Publisher: Elsevier
ISSN: 0272-8842
Date of Acceptance: 17 November 2010
Last Modified: 01 Nov 2022 10:57
URI: https://orca.cardiff.ac.uk/id/eprint/93350

Citation Data

Cited 55 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item