The effect of blood contamination on the compressive strength and surface microstructure of mineral trioxide aggregate

Nekoofar, Mohammad Hossein, Stone, David F. and Dummer, Paul Michael Howell ORCID: https://orcid.org/0000-0002-0726-7467 2010. The effect of blood contamination on the compressive strength and surface microstructure of mineral trioxide aggregate. International Endodontic Journal 43 (9) , pp. 782-791. 10.1111/j.1365-2591.2010.01745.x

Full text not available from this repository.

Abstract

Aim To investigate the effects of whole, fresh human blood contamination on compressive strength and surface microstructure of grey and tooth-coloured mineral trioxide aggregate (MTA). Methodology The materials investigated were grey ProRoot (R) MTA Original (Dentsply Tulsa Dental, Johnson City, TN, USA) and tooth-coloured ProRoot (R) MTA (Dentsply Tulsa Dental). Three groups of 10 custom-made cylindrical moulds (internal dimensions 6 +/- 0.1 mm length and 4 +/- 0.1 mm diameter) were filled with tooth-coloured MTA. In the control group, MTA was mixed with water and exposed to water. In the second group, MTA was mixed with water and exposed to whole, fresh human blood. In the third group, MTA was mixed with and exposed to whole, fresh human blood. These three groups were then duplicated using grey MTA, creating a total of 60 samples. A predetermined amount of MTA and appropriate liquid were triturated in a plastic mixing capsule then subjected to ultrasonic energy after placement in the moulds. After 4 days of incubation, specimens were subjected to compressive strength testing. The surface microstructure of one extra specimen in each group was examined using scanning electron microscopy. Data were subjected to a two-way anova. Results Regardless of MTA type, the mean compressive strength values of both experimental groups, which were in contact with blood, were significantly less than that of the control groups (P < 0.0001). In experimental groups in which MTA was mixed with water and exposed to blood, there was a significant difference (P < 0.0001) in compressive strength between tooth-coloured MTA (30.37 +/- 10.16 MPa) and grey MTA (13.92 +/- 3.80 MPa). Conclusion When blood becomes incorporated into MTA, its compressive strength is reduced. In clinical situations in which blood becomes mixed with MTA, its physical properties are likely to be compromised.

Item Type:	Article
Date Type:	Publication
Status:	Published
Schools:	Dentistry Medicine
Uncontrolled Keywords:	blood contamination; compressive strength; Mineral Trioxide Aggregate; MTA; SEM
Publisher:	Wiley
ISSN:	0143-2885
Last Modified:	18 Oct 2022 13:57
URI:	https://orca.cardiff.ac.uk/id/eprint/16004

Citation Data

Cited 69 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item